Hot Dip Galvanized Product Price, please free to contact us.
LY Steel hot dip galvanizing line with designed annual production capacity of 380,000 ton has the capacity to produce hot dip galvanized steel and hot dip galvalume steel. LY Steel has produced excellent corrosion-resis-tance hot dip galvanized (galvalume) steel with process of advanced electrolytic cleaning, automatic scraper cleaning, online coating weight monitoring system, anti-finger print/environmental passivation roller coating,which are widely used in household appliance, construction, door, process instrumentation and automotive in-dustries.
Coated sheet are classified into
Hot dip galvanized (GI) sheet and strip
Standard steel grades of Janpan, Europe and USA norm, eg. DX51D～DX56D,S220GD～S550GD,H180YD~H300YD,H260LAD~H420LAD,BH220+Z,H450DPD+Z,H600DPD+Z,SGCC,SGC400,
CSTYPEA+Z,CSTYPEB+Z,etc.
Hot dip galvanized (GI) sheet
Grade and Application of Hot Dip Galvanized
Hot dip galvanized sheet of LY Steel are produced from cold rolled substrate with various strength and thick-ness, hot dipped on two surfaces with a layer of metal zinc to prevent corrosion, which features in the perfor-mance of Zn electrochemical protection.
| Steel grades | Application | Features | Executive norms |
| DX51D+Z | Common bending and formability | The product features in good ductility, apply for simple forming, bending and welding. | EN 10346-2009 |
| CSTYPEB+Z | ASTM A653/A653M-09a | ||
| CSTYPEA+Z | |||
| SGCC | JIS G3302-2010 | ||
| DX52D+Z | DQ | The product features in fine formability, apply to spare parts by drawing | EN 10346-2009 |
| DX53D+Z | DDQ | The product features in excellent deep-drawing performance and good ductility, apply to spare parts by deep-drawing and complex forming | |
| DX54D+Z | EDDQ | The product features in better ductility than DDQ, apply to spare parts by EDDQ and more complex forming. | |
| DX56D+Z | |||
| S220GD+Z | Structural | The product features in high strength with normal processability, apply for simple forming, bending and welding. | |
| S250GD+Z | |||
| S280GD+Z | |||
| S320GD+Z | |||
| S350GD+Z | |||
| S550GD+Z | |||
| H450DPD+Z | dual-phase steel | It has good resistance to corrosion fatigue wear and corrosion resistance, have higher strength and fatigue strength, good weldability, cracking tend to be small. | EN 10346-2009 |
| H600DPD+Z | |||
| H260LAD+Z | high-strength steel | Steel strength can be obviously improved, good machinability and corrosion resistance. | EN 10346-2009 |
| H300LAD+Z | |||
| H340LAD+Z | |||
| H380LAD+Z | |||
| H420LAD+Z | |||
| LGAF+Z | Chrome-free | Excellent fingerprint resistance and lubricity, can be undercoatofthickcoating | Technical standard on fingerprint resistance |
| LGDG1+Z | Rail steel | Excellentrollformingpropertyandsaltsprayproperty,canbe appliedonguiderailandsliderail | Technical standard on rail steel |
| LGDG2+Z | |||
| LGDG1+Z2 | |||
| H180YD+Z | IF high strength | HighstrengthIFsteelwithgooddeepdrawabilityandstrength wasappliedinautomotivecomponentprocessing. | EN 10346-2009 |
| H220YD+Z | |||
| H260YD+Z | |||
| H300YD+Z | |||
| SGC340 | Structural application | The product features in high strength with normal processability, apply for simple forming, bending and welding. | JIS G3302-2010 |
| SGC400 |
Surface quality
| Grading | Code | Features |
| Common surface | FA | Detective surface is allowable, eg. Checkered bumps, dent, scratches, blisters, different micro-structure, dark spots, stripes and small passivation spots, etc. as well as tension levelling marks and zinc fluctuation marks. Cracks and slip lines is possible. |
| Fine surface | FB | FB could be reached after skin pass. Small-scale imperfection is allowable, eg. tension levelling marks, skin pass marks, slight scratches, surface structure, zinc fluctuation marks and passivation defect. |
| Excellent surface | FC | FB could be reached after skin pass. Non of any adverse effect of the higher-quality side on aspect after painting, the other surface shall meet the requirement of FB at least. |
Recommended standard coating weight
| Coating pattern | Pure zinc coating |
| Uniform thickness | Z60/Z80/Z100/Z120/Z150/Z180/Z220/Z250/Z275 |
| Differential thickness | Each side:30，40，50，60，75，90，110，125，130，150 |
| Remark: The coils with other coating weight could be supplied through negotiation between the supply and demand sides. | |
Coating thickness
| Coating thickness | Pure zinc coating |
| Uniform thickness | 30/30~135/135 |
| Differential thickness | 30~150(each side) |
| Remark: The maximum thickness difference ratio of differential thickness is 1:3. | |
Surface post-processing
| Surface processing | Explanation |
| Chromatizing | To prevent exposed to moisture, corrosive risk less during transporation and storage. Local color spots on surface is possible after chromatizing, without affecting any product quality. |
| Chromate-free passivation | To prevent exposed to moisture, corrosive risk less during transporation and storage. The processing is characterized by the satisfaction of environment protection requirements. |
| Oiling | Surface early corrosive risk less, to prevent corrosion during transporation and storage. |
| Chromatizing + oiling | Double antiseptic of chromatizing and oiling |
| Chromate-freepassivation+ oiling(GI) | Double antiseptic of chromate-free passivation and oiling with satisfaction of environment protection requirements |
| Chromate-free anti-finger print (GL) | One razor-thin layer of organic coating on surface provides additional anti-corrosion protection as well as finger print resistance, which could improve lubricating property during forming and act as basement of subsequent coatings with satisfaction of environment protection requirements. |
| Remark: Mixed processing of GI and GL is applied for the surface without identifying GI or GL. | |
Performane of GI product
| Product | GI | |
| Coating type | ||
| Processability |
| |
| Thermotolerance | Non-discoloring for long term use at 230℃ , but color change in exceed of 250℃ | |
| Corrosion resistance | The electrochemical protection of GI coating on steel is better than that of oil paint and plastic layer, higher collision-resistance and scratch-resistance without peeling off for decades. | |
| Coating | Smooth coating film could be obtained through selection of zinc spangle |
Anti-corrosion property
| Test time | 350h | 1200h | 350h | 1200h |
| Galvanizing type and weight | GI,90/90g/m | |||
| Test standard | ASTM B117 | |||
Air exposed test