ASTM A213, A213M ASME SA213 / SA213M

Material/Steel Grade: TP304, TP304L, TP304H, TP310, TP310S, TP316, TP316L, TP316Ti, TP317, TP317L, TP321, TP321H, TP347, TP347H
Application: Seamless Austenitic Alloy-Steel Boiler, Super Heater and Heat-Exchanger Tubes
Size: OD: 6.0~50.8mm WT: 0.8~10.0mm
Finish: Mill

Heat Treatment Requirements

Grade UNS
Designation
Heat Treat Type Austenitizing/ Solutioning Temperature, min or range °F [°C] Cooling Media ASTM Grain Size No. B
TP304 S30400 Solution treatment 1900 °F [1040 °C] water or another rapid cool . . .
TP304L S30403 Solution treatment 1900 °F [1040 °C] water or another rapid cool . . .
TP304H S30409 Solution treatment 1900 °F [1040 °C] water or another rapid cool 7
TP309S S30908 Solution treatment 1900 °F [1040 °C] water or another rapid cool . . .
TP309H S30909 Solution treatment 1900 °F [1040 °C] water or another rapid cool 7
TP310S S31008 Solution treatment 1900 °F [1040 °C] water or another rapid cool . . .
TP310H S31009 Solution treatment 1900 °F [1040 °C] water or another rapid cool 7
TP316 S31600 Solution treatment 1900 °F [1040 °C] water or another rapid cool . . .
TP316L S31603 Solution treatment 1900 °F [1040 °C] water or another rapid cool . . .
TP316H S31609 Solution treatment 1900 °F [1040 °C] water or another rapid cool 7
TP317 S31700 Solution treatment 1900 °F [1040 °C] water or another rapid cool . . .
TP317L S31703 Solution treatment 1900 °F [1040 °C] water or another rapid cool . . .
TP321 S32100 Solution treatment 1900 °F [1040 °C] water or another rapid cool . . .
TP321H S32109 Solution treatment cold worked:2000[1090] hot rolled: 1925 [1050]H water or another rapid cool 7
TP347 S34700 Solution treatment 1900 °F [1040 °C] water or another rapid cool . . .
TP347H S34709 Solution treatment cold worked:2000[1100] hot rolled: 1925 [1050]H water or another rapid cool 7
TP444 S44400 subcritical anneal . . . . . . . . .